KML 925E is a compound functional masterbatch with anti-adhesion and smooth effect. High purity spherical silicon opening agent and imported erucamide slip agent are added to make the processed film have efficient anti-adhesion and smooth effect, and at the same time can obtain better optical properties.

Message

Product Details

● Product description

● Physical properties

Melt index (190 ℃/2.16kg)	g/10min	14
Bulk density	kg/m³	590
Moisture content	ppm	<1500
active ingredient content	%	15

The above is only typical data, not as a standard at the time of sale.

● Application

According to the customer's requirements for performance, the addition amount is 0.5~3.0%, and the recommended dosage is generally as follows:

Film thickness (μm)	25	50	75	100	150
Addition amount (%)	3.0	2.0	1.0	0.7	0.5

Note: The specific amount of addition, please customers according to different film thickness and smooth requirements through experiments to obtain the amount of this recommend is for reference only. If an excessive amount of KML 925E is added, it may cause the screw to slip, poor adhesion of printing ink, poor heat sealing and poor adhesive strength, etc. It is necessary to evaluate the addition amount. And anti-static, UV stable masterbatch and other mixed use may produce smooth synergistic effect.

● Food approval

KML 925E can be applied to food packaging FDA unlimited according to the following requirements

● Packaging & Storage

KML 925E is packed in polyethylene bags of 25kg each, covered with shrink film and carried on pallets. For optimum performance, the storage period should preferably not exceed 6 months at a temperature of 25°C.