KML 1056A is a compound functional masterbatch with anti-adhesion and high smooth effect at the same time. It is added with high purity silica opening agent and erucic acid amide slip agent, with high cost performance, remarkable effect and wide application range.

Message

Product Details

● Product description

● Physical properties

Melt index (190 ℃/2.16kg)	g/10min	4
Bulk density	kg/m3	560
Moisture content	ppm	<1500
active ingredient content	%	15

The above is only typical data, not as a standard at the time of sale.

● Method of use

According to the customer's requirements for performance, the addition amount is 0.5~3.0, and the general recommended addition amount is as follows:

Film thickness (μm)	25	50	75	100	150
Addition amount (%)	2.5	1.5	1.0	0.7	0.5

Note: The specific addition amount is obtained through experiments according to different film thickness and smooth requirements. The dosage of this recommend is for reference only. If an excessive amount of KML 1056A is added, it may cause problems such as screw slippage, poor adhesion of printing ink, poor heat sealing and poor adhesive strength. It is necessary to evaluate the amount of addition. And anti-static, UV stable masterbatch and other mixed use may produce smooth synergistic effect.

● Food approval

KML 1056A can be applied to food packaging according to the following requirements

FDA No Restrictions

● Packaging & Storage

KML 1056A is packed in polyethylene bags of 25kg each, covered with shrink film and carried on pallets. For optimum performance, the storage period should preferably not exceed 6 months at a temperature of 25°C.